ISO 6721-9:2019
2019-04
Тезис
This document describes a pulse propagation method for determining the storage component of the complex tensile modulus E' of polymers at discrete frequencies typically in the range 3 kHz to 10 kHz. The method is suitable for measuring materials with storage moduli in the range 0,01 GPa to 200 GPa and with loss factors below 0,1 at around 10 kHz. With materials having a higher loss, significant errors in velocity measurement are introduced through decay of amplitude.
The method allows measurements to be made on thin films or fine fibres and long specimens, typically tapes of 300 mm × 5 mm × 0,1 mm or fibres of 300 mm × 0,1 mm (diameter).
This method may not be suitable for cellular plastics, composite plastics and multilayer products.
Общая информация
-
Текущий статус: ОпубликованоДата публикации: 2019-04Этап: Систематический пересмотр между-народного стандарта [90.20]
-
Версия: 2
-
Технический комитет :ISO/TC 61/SC 5ICS :83.080.01
- RSS обновления
Жизненный цикл
-
Ранее
ОтозваноISO 6721-9:1997
ОтозваноISO 6721-9:1997/Amd 1:2007
-
Сейчас
ОпубликованоISO 6721-9:2019
Стандарт, который пересматривается каждые 5 лет
Этап: 90.20 (Hа стадии пересмотра)-
00
Предварительная стадия
-
10
Стадия, связанная с внесением предложения
-
20
Подготовительная стадия
-
30
Стадия, связанная с подготовкой проекта комитета
-
40
Стадия, связанная с рассмотрением проекта международного стандарта
-
50
Стадия, на которой осуществляется принятие стандарта
-
60
Стадия, на которой осуществляется публикация
-
90
Стадия пересмотра
-
95
Стадия, на которой осуществляется отмена стандарта
-
00
Появились вопросы?
Ознакомьтесь с FAQ
Часы работы:
Понедельник – пятница: 09:00-12:00, 14:00-17:00 (UTC+1)